Biological Properties of Regenerated Silk Fibroin Films

The aim of the investigation was to study the biological and mechanical properties of silk fibroin films and composite silk fibroin films containing 30% collagen by weight.

Materials and Methods. All films were prepared by casting method using water and formic acid as solvents. Scanning electron microscopy and atomic force microscopy were applied. Human hepatoblastoma cell line Hep-G₂ was used to test film compatibility.

Results. We studied surface roughness degree of the obtained films. Water-based films were found to have permeability for low molecular weight substances. Tensile strength and elasticity indices were measured for all types of films. Collagen added to film composition was revealed to have no significant effect on tensile strength, though it increased film elasticity. We studied the degradation of films. Collagen was shown to have no significant impact on film degradation rate both in phosphate-buffer saline and oxidizing media. We demonstrated with an example of cell line Hep-G₂ that water-based films exhibit higher proliferative activity.

Conclusion. Silk fibroin water solution has the best properties to develop films for tissue engineering.

1. Moisenovich M.M., Pustovalova O., Shackelford J., Vasiljeva T.V., Druzhinina T.V., Kamenchuk Y.A., Guzeev V.V., Sokolova O.S., Bogush V.G., Debabov V.G., Kirpichnikov M.P., Agapov I.I. Tissue regeneration in vivo within recombinant spidroin 1 scaffolds. Biomaterials 2012; 33(15): 3887–3898, http://dx.doi.org/10.1016/j.biomaterials.2012.02.013.
2. Bonartsev A., Yakovlev S., Boskhomdzhiev A., Zharkova I., Bagrov D., Myshkina V., Mahina T., Kharitonova E., Samsonova O., Zernov A., Zhuikov V., Efremov Y., Voinova V., Bonartseva G., Shaitan K. The terpolymer produced by Azotobacter chroococcum 7B: effect of surface properties on cell attachment. PLoS One 2013; 8(2): e57200, http://dx.doi.org/10.1371/journal.pone.0057200.
3. Moisenovich M.M., Pustovalova O.L., Arhipova A.Y., Vasiljeva T.V., Sokolova O.S., Bogush V.G., Debabov V.G., Sevastianov V.I., Kirpichnikov M.P., Agapov I.I. In vitro and in vivo biocompatibility studies of a recombinant analogue of spidroin 1 scaffolds. J Biomed Mater Res A 2011; 96(1): 125–131, http://dx.doi.org/10.1002/jbm.a.32968.
4. He Y.-H., Zhang N.-N., Li W.-F., Jia N., Chen B.-Y., Zhou K., Zhang J., Chen Y., Zhou C.-Z. N-terminal domain of Bombyx mori fibroin mediates the assembly of silk in response to pH decrease. J Mol Biol 2012; 418(3–4): 197–207, http://dx.doi.org/10.1016/j.jmb.2012.02.040.
5. Kasoju N., Bora U. Silk fibroin based biomimetic artificial extracellular matrix for hepatic tissue engineering applications. Biomed Mater 2012; 7(4): 045004, http://dx.doi.org/10.1088/1748-6041/7/4/045004.
6. Hu Y., Zhang Q., You R., Wang L., Li M. The relationship between secondary structure and biodegradation behavior of silk fibroin scaffolds. Advances in Materials Science and Engineering 2012; 2012: 185905, http://dx.doi.org/10.1155/2012/185905.
7. Baran E.T., Tuzlakoğlu K., Mano J.F., Reis R.L. Enzymatic degradation behavior and cytocompatibility of silk fibroin–starch–chitosan conjugate membranes. Materials Science and Engineering 2012; 32(6): 1314–1322, http://dx.doi.org/10.1016/j.msec.2012.02.015.
8. Moisenovich M.M., Arkhipova A.Y., Orlova A.A., Drutskaya M.S., Volkova S.V., Zacharov S.E., Agapov I.I., Kirpichnikov M.P. Composite scaffolds containing silk fibroin, gelatin, and hydroxyapatite for bone tissue regeneration and 3D cellc. Acta Naturae 2014; 6(1): 96–101.
9. Agapov I.I., Moisenovich M.M., Druzhinina T.V., Kamenchuk Y.A., Trofimov K.V., Vasilyeva T.V., Konkov A.S., Arhipova A.Y., Sokolova O.S., Guzeev V.V., Kirpichnikov M.P. Biocomposite scaffolds containing regenerated silk fibroin and nanohydroxyapatite for bone tissue regeneration. Dokl Biochem Biophys 2011; 440: 228–230, http://dx.doi.org/10.1134/S1607672911050103.
10. Chandrakasan G., Torchia D.A., Piez K.A. Preparation of intact monomeric collagen from rat tail tendon and skin and the structure of the nonhelical ends in solution. J Biol Chem 1976; 251(19): 6062–6067.
11. Kjaer M. Role of extracellular matrix in adaptation of tendon and skeletal muscle to mechanical loading. Physiol Rev 2004; 84(2): 649–698, http://dx.doi.org/10.1152/physrev.00031.2003.
12. Zhang Q., Zhao Y., Yan S., Yang Y., Zhao H., Li M., Lu S., Kaplan D.L. Preparation of uniaxial multichannel silk fibroin scaffolds for guiding primary neurons. Acta Biomaterialia 2012; 8(7): 2628–2638, http://dx.doi.org/10.1016/j.actbio.2012.03.033.
13. Rosenow F., Ossig R., Thormeyer D., Gasmann P., Schlüter K., Brunner G., Haier J., Eble J.A. Integrins as antimetastatic targets of RGD-independent snake venom components in liver metastasis. Neoplasia 2008; 10(2): 168–176.
14. She Z., Jin C., Huang Z., Zhang B., Feng Q., Xu Y. Silk fibroin/chitosan scaffold: preparation, characterization, and culture with HepG2 cell. J Mater Sci Mater Med 2008; 19(12): 3545–3553, http://dx.doi.org/10.1007/s10856-008-3526-y.
15. Lv Q., Feng Q., Hu K., Cui F. Three-dimensional fibroin/collagen scaffolds derived from aqueous solution and the use for HepG2 culture. Polymer 2005; 46(26): 12662–12669, http://dx.doi.org/10.1016/j.polymer.2005.10.137.
16. Hu K., Lv Q., Cui F.Z., Feng Q.L., Kong X.D., Wang H.L., Huang L.Y., Li T. Biocompatible fibroin blended films with recombinant human-like collagen for hepatic tissue engineering. Journal Bioactive and Compatible Polymers 2006; 21(1): 23–37, http://dx.doi.org/10.1177/0883911506060455.

Safonova L.А., Bobrova М.М., Agapova О.I., Kotliarova М.S., Arkhipova А.Yu., Moisenovich М.М., Agapov I.I. Biological Properties of Regenerated Silk Fibroin Films. Sovremennye tehnologii v medicine 2015; 7(3): 6, https://doi.org/10.17691/stm2015.7.3.01